自粘涂层硅钢B35A270-Z

电工钢硅钢片Ultra-thin series: B15AHT1000, B15AHT1200, B15AT1000, B15AT1200B15AT1500, B15AT1550, B20AHT1000, B20AHT1200, B20AT1000, B20AT1200, B20AT1500, 20WTG1200, 20WTG1500 20WTG1550 B25AHV1200 B25AHV1300, B27AHV1400, B27AV1400, B30AHV1500 B30AHV1400, B35AV1700 B35AV1800High performance series: B35AH300, B50AH300, 50AH470, 50AH600, 50AH800, B50AH470, B50AH600, B50AH800, B50AR300, B50AR600, B50AR500, B50AR350, B20AT15000.35 series: B35A200, B35A210, B35A230, B35A250, B35A270,B35A300, B35A360, B35A440, B35A550, B35AH300, B35AR300, B35AY-10.5 series: B50A250, B50A270, B50A290, B50A310, B50A350, B50A400, B50A470, B50A600, B50A700, B50A800, B50A1000, B50A13000.65 series: B65A470, B65A530, B50A600B65A700, B65A800 B65A1000, B65A1300Super thick Series: 70WK340, 75WK400, 80WK420, 85WK450, 10W800 WFC-100A, silicon steel sheet performance: A low iron loss. As an important indicator of quality, each country divides the grade by the iron loss value. The lower the iron loss, the higher the grade and the higher the quality.B. High magnetic induction strength. Under the same magnetic field, the silicon steel sheet with high magnetic sensitivity can be obtained. The volume and weight of the iron core of the motor or transformer made by it are relatively small, which can save silicon steel sheet, copper wire and insulating materials, etc.C. High stacking coefficient. The surface of the silicon steel sheet is smooth, flat and uniform in thickness, which improves the stacking coefficient of the iron core.D. Good punching property. This is more important for manufacturing small and micro motor iron cores.E. The surface has good adhesion and weldability to the insulating film.

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating